Please use this identifier to cite or link to this item: http://repositorio.uisek.edu.ec/handle/123456789/3450
Title: Caracterización de membrana polimérica de PVC y HDPE de alta densidad más comunes en Ecuador para determinar aplicaciones automotrices
Authors: Martínez Gómez, Javier
Torres Andrade, Felipe Santiago
Keywords: DISEÑO MECÁNICO
VEHÍCULO AUTOMOTOR
PIEZAS DE VEHÍCULOS
PLÁSTICOS
MATERIALES RESISTENTES AL CALOR
Issue Date: Aug-2019
Publisher: Universidad Internacional SEK
Citation: CT-MDMAV T693c/2019
Abstract: El propósito de esta investigación es determinar las características necesarias de la membrana polimérica de PVC y HDPE, dentro de las cuales destacan sus buenas propiedades físicas, térmicas, bajo costo y alta resistencia a la intemperie. Los beneficios del estudio recaen en la utilización de las membranas no sólo en la ingeniería civil, sino evidenciar los comportamientos mecánicos de las geomembranas de PVC y HDPE de 1mm y 1.5 para lograr una comparación entre ellas y determinar los distintos esfuerzos que soportan y a su vez comprobar su utilidad en otras áreas de la ingeniería. Se comparan los resultados obtenidos de dos membranas PVC y HDPE en dos espesores diferentes, considerando variables controlables como tensión, alargamiento a la rotura, temperatura de trabajo entre otras. Dichas pruebas están sometidas a normas ASTM las cuales son cotejadas para determinar la membrana con mejores propiedades. Luego de la comparación se obtiene como resultado que la membrana de HDPE 1500 posee una resistencia al rasgado 142.33 N con extensión 47.70 mm y una resistencia a la rotura de 11.53 MPA, la membrana de HDPE 1000 posee una resistencia al rasgado 102.58 N, con extensión 50.11 mm y una resistencia a la rotura de 11.93 MPA, la membrana de PVC 1500 posee una resistencia al rasgado 77.33 N con extensión 33.49 mm y una resistencia a la rotura de 10.06 MPA, la membrana de PVC 1000 posee una resistencia al rasgado 55.83 N, extensión 34.20 mm y una resistencia a la rotura de 9.41 MPA. De los datos antes mencionados se concluye que las membranas de PVC soportan menor fuerza que las de HDPE, pero al comparar con las del plástico tradicional estas conservan muchas características importantes dando un factor de seguridad más alto que el ABS, por lo que pueden ser utilizadas en diferentes ramas y aplicaciones.
Description: The purpose of this investigation is to determine the necessary characteristics of the PVC and HDPE polymeric membrane, among which its good physical, thermal, low cost and high weather resistance. The benefits of the study lie in the use of membranes not only in civil engineering, but also in demonstrating the mechanical behaviors of PVC and HDPE geomembranes of 1mm and 1.5 to achieve a comparison between them and determine the different efforts they support and in turn Check its usefulness in other areas of engineering. The results obtained from two PVC and HDPE membranes are compared in two different thicknesses, considering controllable variables such as tension, elongation at break, working temperature among others. These tests are subject to ASTM standards which are compared to determine the membrane with the best properties to be used in the automotive field. Then, the comparison is obtained as a result that the HDPE 1500 membrane has a tear strength 142.33 N with extension 47.70 mm and a tear strength of 11.53 MPA, the HDPE 1000 membrane has a tear resistance 102.58 N, with extension 50.11 mm and a tear strength of 11.93 MPA, the PVC 1500 membrane has a tear resistance 77.33 N with a 33.49 mm extension and a tear resistance of 10.06 MPA, the PVC 1000 membrane has a tear resistance 55.83 N , extension 34.20 mm and a breaking strength of 9.41 MPA. From the data before determining, it is concluded that PVC membranes withstand less force than those of HDPE, but when compared with those of traditional plastic they definitely retain many important characteristics giving a higher safety factor than ABS so they can be Used in different branches and applications
URI: http://repositorio.uisek.edu.ec/handle/123456789/3450
Appears in Collections:Maestría en Diseño Mecánico mención Fabricación de Autopartes de Vehículo

Files in This Item:
File Description SizeFormat 
Presentación F TORRES.pdf1,44 MBAdobe PDFView/Open
Tesis 7I8I2019.pdf5,16 MBAdobe PDFView/Open
D1004.27409.pdf99,72 kBAdobe PDFView/Open
D1204.30218.pdf72,75 kBAdobe PDFView/Open
D1525.19484.pdf232,6 kBAdobe PDFView/Open
D2582.39077.pdf138,36 kBAdobe PDFView/Open
D638.38935.pdf358,8 kBAdobe PDFView/Open
D751.3732.pdf350,69 kBAdobe PDFView/Open
D882.19019.pdf177,25 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.